EN 10216-2 Efnasamsetning
|
Stálgráða |
C |
Si |
Mn |
P |
S |
Kr |
Mo |
Ni |
Altot |
Cu |
Ti max |
|
|
Stál nafn |
Stálnúmer |
hámark |
hámark |
|||||||||
|
P195GH |
1.0348 |
=0.13 |
=0.35 |
=0.70 |
0.025 |
0.020 |
=0.30 |
=0.08 |
=0.30 |
=0.020 |
=0.30 |
0.040 |
|
P235GH |
1.0345 |
=0.16 |
=0.35 |
=1.20 |
0.025 |
0.020 |
=0.30 |
=0.08 |
=0.30 |
=0.020 |
=0.30 |
0.040 |
|
P265GH |
1.0425 |
=0.20 |
=0.40 |
=1.40 |
0.025 |
0.020 |
=0.30 |
=0.08 |
=0.30 |
=0.020 |
=0.30 |
0.040 |
|
16Mo3 |
1.5415 |
0.12-0.20 |
0.40-0.90 |
0.40-0.90 |
0.025 |
0.020 |
=0.30 |
0.25-0.35 |
=0.30 |
=0.040 |
=0.30 |
|
|
14MoV6-3 |
1.7715 |
0.10-0.15 |
0.15-0.35 |
0.40-0.70 |
0.025 |
0.020 |
0.30-0.60 |
0.40-0.50 |
=0.30 |
=0.040 |
=0.30 |
|
|
13CrMo4-5 |
1.7335 |
0.10-0.17 |
=0.15 |
0.40-0.70 |
0.025 |
0.020 |
0.70-1.15 |
0.40-0.60 |
=0.30 |
=0.040 |
=0.30 |
|
|
10CrMo9-10 |
1.7380 |
0.08-0.14 |
0.08-0.14 |
0.30-0.70 |
0.025 |
0.020 |
2.00-2.50 |
0.90-1.10 |
=0.30 |
=0.040 |
=0.30 |
|
|
25CrMo4 |
1.7218 |
0.22-0.29 |
0.22-0.29 |
0.60-0.90 |
0.025 |
0.020 |
0.90-1.20 |
0.15-0.30 |
=0.30 |
=0.040 |
=0.30 |
|
|
15NiCuMoNb5-6-4 |
1.6368 |
=0.17 |
=0.17 |
0.80-1.20 |
0.025 |
0.020 |
=0.30 |
0.25-0.50 |
1.00-1.30 |
=0.050 |
0.50-0.80 |
|
|
X10CrMoVNb9-1 |
1.4903 |
0.08-0.12 |
0.08-0.12 |
0.30-0.60 |
0.025 |
0.020 |
8.00-9.50 |
0.85-1.05 |
=0.40 |
=0.040 |
=0.30 |
|
|
a Hlutum sem ekki eru tilgreindir í þessari töflu má ekki bæta viljandi við stálið nema með samþykki kaupanda, að undanskildum þáttum sem bæta má við til að klára steypuna. Allar viðeigandi ráðstafanir skulu gerðar til að koma í veg fyrir að óæskilegum þáttum úr rusli eða öðrum efnum sem notuð eru í stálframleiðslunni bætist við. |
||||||||||||
|
b Þessi krafa á ekki við að því tilskildu að stálið innihaldi nægilegt magn af öðrum köfnunarefnisbindandi þáttum sem skal tilkynna. Þegar títan er notað skal framleiðandinn sannreyna að (Al+Ti/2)=0,020% |
||||||||||||
|
c Valkostur 2: Til að auðvelda síðari mótunaraðgerðir gilda umsamið hámarks koparinnihald lægra en tilgreint er og umsamið tilgreint hámarks tininnihald |
||||||||||||
|
d Ekki þarf að greina frá innihaldi þessara þátta nema það sé viljandi bætt við leikhópinn |
||||||||||||
|
e Fyrir veggþykkt=30 mm má auka kolefnisinnihaldið um 0,02% fyrir steypu- og vörugreiningu |
||||||||||||
|
f Ekki skal fara yfir efra kolefnisgildið sem er 0,23% fyrir vörugreiningu |
||||||||||||
EN 10216-2 Vélræn eign
|
Stálgráða |
Togeiginleikar við stofuhita |
Áhrifareiginleikar ab |
|||||||||||
|
Stál nafn |
Stálnúmer |
Efri uppskeruþol eða sönnunarstyrkur ReH eða Rp0,2 fyrir veggþykkt T Min. |
Togstyrkur Styrkur Rm |
Lenging A mín. % a |
Lágmarks meðaltal frásogaðrar orku KV J við gráðu hitastig |
||||||||
|
T Minna en eða jafnt og 16 |
160 |
40 |
60 |
l |
t |
l |
t |
||||||
|
MPa |
MPa |
MPa |
MPa |
MPa |
20 |
0 |
-10 |
20 |
0 |
||||
|
P195GH |
1.0348 |
195 |
320-440 |
27 |
25 |
40 c |
28 d |
27c |
|||||
|
P235GH |
1.0345 |
235 |
225 |
215 |
360-500 |
25 |
23 |
40 c |
28 d |
27c |
|||
|
P265GH |
1.0425 |
265 |
255 |
245 |
410-570 |
23 |
21 |
40 c |
2s d |
27C |
|||
|
16Mo3 |
1.5415 |
280 |
270 |
260 |
450-600 |
22 |
20 |
40 c |
27 c |
||||
|
14MoV6-3 |
1.7715 |
320 |
320 |
310 |
460-610 |
20 |
18 |
40 c f |
27 c |
||||
|
13CrMo4-5 |
1.7335 |
290 |
290 |
280 |
440-590 |
22 |
20 |
40 c |
27 c |
||||
|
10CrMo9-10 |
1.7380 |
280 |
280 |
270 |
480-630 |
22 |
20 |
40 c |
27 c |
||||
|
25CrMo4 |
1.7218 |
345 |
345 |
345 |
540-690 |
18 |
15 |
40 c f |
27 c |
||||
|
15NiCuMoNb5-6-4 |
1.6368 |
440 |
440 |
440 |
440e |
610-780 |
19 |
17 |
40 c f |
27 c |
|||
|
X10CrMoVNb9-1 |
1.4903 |
450 |
450 |
450 |
450 |
630-830 |
19 |
17 |
40 c f |
27 c |
|||
|
a I=langsum t=þversum |
|||||||||||||
|
b Staðfesta þegar valkostir 4 og/eða 5 eru tilgreindir, nema neðanmálsgrein f) eigi við |
|||||||||||||
|
c Valkostur 4: Staðfesta skal höggorku. |
|||||||||||||
|
d Valkostur 5: Staðfesta skal höggorku á lengd. |
|||||||||||||
|
e Fyrir veggþykkt 60 mm< T =80mm |
|||||||||||||
|
f Höggprófun áskilin fyrir veggþykkt T =16mm |
|||||||||||||
EN 10216-2 ketilrör Hitameðferð
|
Stálgráða |
Hitameðferð a |
Austenizing |
Hitun |
|||
|
Stál nafn |
Stálnúmer |
Hitastig gráðu |
Kælimiðill |
Hitastig gráðu |
Kælimiðill |
|
|
P195GH |
1.0348 |
+N b |
880 til 940 |
Loft |
- |
- |
|
P235GH |
1.0345 |
+N b |
880 til 940 |
Loft |
- |
- |
|
P265GH |
1.0425 |
+N b |
880 til 940 |
Loft |
- |
- |
|
16Mo3 |
1.5415 |
+N b |
890 til 950 |
Loft |
- |
- |
|
14MoV6-3 |
1.7715 |
+NT f.Kr |
930 til 990 |
Loft |
680 til 730 |
lofti |
|
13CrMo4-5 |
1.7335 |
+NT f.Kr |
900 til 960 |
Loft |
660 til 730 |
lofti |
|
10CrMo9-10 |
1.738 |
+NT f.Kr |
900 til 960 |
Loft |
680 til 750 |
lofti |
|
25CrMo4 |
1.7218 |
+QT |
860 til 900 |
Loft eða vökvi |
620 til 680 |
lofti |
|
15NiCuMoNb5-6-4 |
1.6368 |
+NT c |
880 til 980 |
Loft |
580 til 680 |
lofti |
|
X10CrMoVNb9-1 |
1.4903 |
+NT c |
1040 til 1090 |
lofti |
730 til 780 |
lofti |
|
a +N=Normalising, +NT=Normalizing + Tempering, +QT=Slökkun + Tempering (loft eða vökvi), +I=Jafnhitun. |
||||||
|
b Normalizing felur í sér Normalizing Forming. |
||||||
|
c For these steel grades it may be necessary in the case of wall thickness T above 25 mm or T/D >0,15 til að beita slökun og temprun til að ná tilætluðum uppbyggingu og efniseiginleikum. Ákvörðun skal vera í valdi framleiðanda en skal tilkynnt viðskiptavini við fyrirspurn og pöntun. Stálrör sem eru meðhöndluð á þann hátt skulu auðkennd með stálheitinu ásamt tákninu +QT. |
||||||